Innovative and high-quality material consisting of thermoplastic derivate resins, PMMA (polymethylmethacrylate) added with compound for the production of long-lasting temporary crowns and bridges. Use and technical use for the production of long-lasting temporary crowns and bridges.
The disc is homogeneous giving a natural appearance to the final artifact.
Its layering goes from cervical to enamel, with an excellent aesthetic result. The processing can be done either dry or wet.
Full description
The device is in class IIa according to directive 93/42/EEC and subsequent updates.
PMMA milling disc with the following characteristics:
– Reduced residual monomer content
– Ensures greater resistance to plaque and discolouration
– Ensures greater resistance to plaque and discolouration
– Natural colour
– Excellent resistance to abrasion
Available colours:A1-A2-A3-A3,5-C2-C3-D2-D3
Thickness: 16mm and 20mm
Diameter: 98.5 with shoulder
Elasticity Module: >2,22 Mpa
Solubility in water: <0,7 μg/mm³
Flexural strength and elastic modulus: >105 Mpa
Breaking load: >76 Mpa
Residue of monomer (24h a 37°C e 30 min all’aria): <0,6%
Data sheet
| Thickness | 20 mm |
|---|---|
| Color | A1, A2, A3, A3,5, C2, C3, D2, D3 |
Related products
Related products
-
Milling MaterialsPreshaded castable Pmma disc 14 mm
-
Milling Materials
Preshaded castable Pmma disc 18 mm
-
Milling Materials
Preshaded castable Pmma disc 20 mm
-
Milling Materials
Multilayer Pmma disc for temporaries 20 mm